跟著工藝技術(shù)的開展，鋁塑板在人們生活中運(yùn)用的重量越來越高，在色彩方面也不再像曾經(jīng)那樣單調(diào)?，F(xiàn)在的鋁塑板加工
With the development of technology, the weight of aluminium-plastic sheet used in people's life is getting higher and higher, and its color is no longer as monotonous as it used to be. Current Aluminum Plastic Plate Processing
可以對(duì)你想要的顏色進(jìn)行上色，但我們?cè)趯?duì)鋁塑板上色時(shí)，難免會(huì)遇到染不上色的狀況，那么，鋁塑板染不上色的發(fā)生原
You can colour the color you want, but when we colour the aluminium plastic sheet, we will inevitably encounter the situation that the color cannot be dyed. Then, the origin of the color cannot be dyed on the aluminium plastic sheet.
因及處理方法有：
The causes and treatment methods are as follows:
1、陽極氧化膜厚不足：解決的辦法是檢查陽極氧化工藝是否規(guī)范，看溫度，電壓，導(dǎo)電等要素是否穩(wěn)定，若有異
1. Insufficient thickness of anodic oxide film: The solution is to check whether the anodic oxidation process is standardized and whether the factors such as temperature, voltage and conductivity are stable, if different.
常，請(qǐng)相應(yīng)調(diào)整規(guī)范之，若無異常，可恰當(dāng)延長氧化時(shí)間，確保膜厚合格。
Often, please adjust the specifications accordingly. If there is no abnormality, the oxidation time can be prolonged appropriately to ensure that the film thickness is up to standard.
2、染液PH值太高：此刻，可用冰醋酸將PH值調(diào)至規(guī)范值。
2. The PH value of dye solution is too high: at this moment, the PH value can be adjusted to the standard value by glacial acetic acid.
3、氧化后工件在水槽中放置時(shí)間太久：發(fā)起及時(shí)染色，假如這種狀況現(xiàn)已發(fā)生，可將工件放在陽極氧化槽中或硝
3. After oxidation, the workpiece is placed in the tank for too long: initiating timely dyeing, if this situation has occurred, the workpiece can be placed in the anodic oxidation tank or nitrate
酸中和槽中恰當(dāng)活化處理后再進(jìn)行染色，效果會(huì)很好。
Appropriate activation treatment in acid neutralization tank before dyeing can achieve good results.
4、選用染料已分解或霉變：此刻需更換染料，選用適宜染料。
4. Choose dyestuffs that have been decomposed or moulded. At this moment, dyestuffs need to be replaced and suitable dyestuffs should be selected.

5、氧化溫度過低，導(dǎo)致皮膜致密：可恰當(dāng)進(jìn)步氧化溫度。
5. Low oxidation temperature results in dense skin film: oxidation temperature can be properly improved.
6、導(dǎo)電不良：可能陽極銅桿或陰極鉛板接觸不良所示批量導(dǎo)電不良。留意清洗陽極銅桿及陰極鉛板，確保導(dǎo)電良
6. Poor conductivity: Batch conductivity shown by poor contact of anode copper rod or cathode lead plate may be poor. Pay attention to cleaning anode copper rod and cathode lead plate to ensure good conductivity
好。
OK.
以上就是關(guān)于鋁塑板染不上色的發(fā)生原因及處理方法，現(xiàn)在，鋁塑板現(xiàn)已成為建筑范疇的常用材料，其廣泛用于大樓
Above is about the causes and treatment methods of stainless aluminium-plastic sheet. Now, aluminium-plastic sheet has become a common building material, which is widely used in buildings.
外墻、室內(nèi)墻面、廣告招牌等裝修用范疇。然而跟著人們對(duì)裝修用品的美觀要求越來越高，色彩單一、圖畫呆板的鋁塑板
Exterior walls, interior walls, advertising signs and other decoration areas. However, along with people's increasingly high aesthetic requirements for decoration supplies, single color, stiff drawing of aluminum-plastic sheet
現(xiàn)已無法滿意出產(chǎn)需求。
It is no longer able to satisfy the production demand.
以上信息是我們鋁板生產(chǎn)廠家整理發(fā)布希望對(duì)大家有點(diǎn)幫助我們的網(wǎng)站是：http://m.liyukeji.com！
The above information is our aluminium plate manufacturer collation and release hope to help you a little bit: http://m.liyukeji.com!